National Chung Hsing University Institutional Repository - NCHUIR > 工學院 > 工學院 > 依資料類型分類 > 期刊論文 >  Characterization of the Ti-doped diamond-like carbon coatings on a type 304 stainless steel

Please use this identifier to cite or link to this item: http://nchuir.lib.nchu.edu.tw/handle/309270000/128630

標題: Characterization of the Ti-doped diamond-like carbon coatings on a type 304 stainless steel
作者: Hsieh, W.P.;Wang, D.Y.;Shieu, F.S.
薛富盛
關鍵字: magnetron
日期: 1999
Issue Date: 2012-12-07 14:57:04 (UTC+8)
關連: Journal of Vacuum Science & Technology a-Vacuum Surfaces and Films, Volume 17, Issue 3, Page(s) 1053-1058.
摘要: The microstructure and chemistry of a functionally gradient Ti-doped diamond-like carbon (DLC) coating prepared by a closed field unbalanced magnetron sputtering system (CFUBMS) on a type 304 stainless steel was analyzed by transmission electron microscopy (TEM), electron energy loss spectroscopy (EELS), and scanning electron microscopy (SEM). Three distinct regions including the steel substrate, Ti interlayer, and the functionally gradient coating are observed from the cross-section TEM micrograph. Further analysis of the graded coating using selected area diffraction reveals that the early deposited film is mainly composed of TiN located next to the Ti interlayer; subsequently it changes to a mixture of TiCo0.7N0.3 and TIG, and finally a very complicated mixture containing Ti, TiC, graphite, possibly diamond and amorphous carbon near the coating surface is observed. The graded Ti-doped DLC coating exhibits columnar structure and preferred orientation illustrated by the arced electron diffraction patterns. Chemical analysis carried out by EELS of the surface coating layer using the plan-view TEM specimen indicates that the bonding state of carbon in the Ti-doped DLC coating depends on the content of Ti. For a Ti-rich region, the carbon K edge favors the formation of a TI-C bond, whereas graphitic and/or amorphous carbon dominates in the Ti-deficient regions. In addition, the coated specimens were immersed in a 60% H3PO4 (85 + %) and 40% H2SO4 (95 + %) solution to investigate their corrosion resistance and then examined by SEM and energy-dispersive x-ray spectroscopy (EDS). It is found that the surface coating layer, in which microcracks were observed in the plan-view TEM micrograph, has lower packing density than the subsurface coating. By analysis of the secondary and backscattered electron images, and x-ray mapping, it is believed that the submicron-sized particles that survived the corrosion test in the Ti-doped DLC coating are diamond microcrystallites. (C) 1999 American Vacuum Society. [S0734-2101(99)01203-8].
Relation: Journal of Vacuum Science & Technology a-Vacuum Surfaces and Films
Appears in Collections:[依資料類型分類] 期刊論文
[依教師分類] 薛富盛

loading Web of Knowledge data....

Files in This Item:

File SizeFormat
index.html0KbHTML305View/Open


 


學術資源

著作權聲明

本網站為收錄中興大學學術著作及學術產出,已積極向著作權人取得全文授權,並盡力防止侵害著作權人之權益。如仍發現本網站之數位內容有侵害著作權人權益情事者,請權利人通知本網站維護人員,將盡速為您處理。

本網站之數位內容為國立中興大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用。

聯絡網站維護人員:wyhuang@nchu.edu.tw,04-22840290 # 412。

DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU/NCHU Library IR team Copyright ©   - Feedback